INCOLOY® alloy 800H/800HT UNS N08810/UNS N08811
| Alloy | element | C | Si | Mn | S | Cu | Ni | Cr | Al | Ti | Fe | Al+Ti |
|
Incoloy 800H/HT |
Min | 0.05 | 30.0 | 19.0 | 0.15 | 0.15 | 39.0 | 0.30 | ||||
| Max | 0.10 | 1.0 | 1.5 | 0.05 | 0.75 | 35.0 | 23.0 | 0.60 | 0.60 | 1.20 | ||
| Remark | Incoloy 800HT: C:0.06~0.10,Al+Ti:0.85~1.20. | |||||||||||
|
Aolly Status |
Tensile strength Rm Mpa Min |
Yield strength R P 0. 2 Mpa Min |
Elongation A 5 % Min |
|
annealed |
448 |
172 |
30 |
|
Density g/cm3 |
Melting Point ℃ |
|
7.94 |
1357~1385 |
Rod, Bar, Wire and Forging Stock - ASTM B 408 & ASME SB 408 (Rod & Bar), ASTM B 564 & ASME SB 564 (Forgings)
Plate, Sheet and Strip - ASTM A240/A 480 & ASME SA 240/SA 480(Plate, Sheet, and Strip), ASTM B 409/B906 & ASME SB 409/SB 906 (Plate, Sheet, and Strip)
Pipe & Tube - ASTM B 407/B829 & ASME SB 407/SB 829 (Seamless Pipe & Tubes), ASTM B 514/B 775 &ASME SB 514/SB 775 (Welded Pipe),ASTM B 515/B 751 & ASME SB 515/SB 751(Welded Tubes)
Other Product Forms - ASTM B 366/ASME SB 366 (Fittings)
● High temperature strength
● High creep rupture strength
● Resistant to oxidation and carburization in high temperature environments
● Good corrosion resistance in many acidic environments
● Good resistance to many sulfur-containing atmospheres
Related products
-
INCOLOY® alloy 254Mo/UNS S31254
254 SMO stainless steel bar, also known as UNS S31254, was originally developed for use in seawater and other aggressive chloride-bearing environments. This grade is considered a very high end austenitic stainless steel; UNS S31254 is often referred to as a “6% Moly” grade due to the molybdenum content; the 6% Moly family has the ability to withstand high temperatures and maintain strength under volatile conditions.
-
INCOLOY® alloy 800 UNS N08800
INCOLOY alloy 800 (UNS N08800) is a widely used material for construction of equipment requiring corrosion resistance, heat resistance, strength, and stability for service up to 1500°F (816°C). Alloy 800 offers general corrosion resistance to many aqueous media and, by virtue of its content of nickel, resists stress corrosion cracking. At elevated temperatures it offers resistance to oxidation, carburization, and sulfidation along with rupture and creep strength. For applications requiring greater resistance to stress rupture and creep, especially at temperatures above 1500°F (816°C).
-
INCOLOY® alloy A286
INCOLOY alloy A-286 is an iron-nickel-chromium alloy with additions of molybdenum and titanium. It is age-hardenable for high mechanical properties. The alloy maintains good strength and oxidation resistance at temperatures up to about 1300°F (700°C). The alloy is austenitic in all metallurgical conditions. The high strength and excellent fabrication characteristics of INCOLOY alloy A-286 make the alloy useful for various components of aircraft and industrial gas turbines. It is also used for fastener applications in automotive engine and manifold components subject to high levels of heat and stress and in the offshore oil and gas industry.
-
INCOLOY® alloy 925 UNS N09925
INCOLOY alloy 925 (UNS N09925) is an age hardenable nickel-iron-chromium alloy with additions of molybdenum, copper, titanium and aluminum. It is designed to provide a combination of high strength and excellent corrosion resistance. The nickel content is sufficient for protection against chloride-ion stress corrosion cracking. The nickel, in conjunction with the molybdenum and copper, also gives outstanding resistance to reducing chemicals. The molybdenum aids resistance to pitting and crevice corrosion. The alloy chromium content provides resistance to oxidizing environments. The titanium and aluminum additions cause a strengthening reaction during heat treatment.
-
INCOlOY® alloy 825 UNS N08825/W.Nr. 2.4858
INCOLOY alloy 825 (UNS N08825) is a nickel-iron-chromium alloy with additions of molybdenum, copper, and titanium .It is designed toprovide exceptional resistance to many corrosive environments. The nickel content is sufficient for resistance to chloride-ion stress-corrosion cracking. The nickel in conjunction with the molybdenum and copper, also gives outstanding resistance to reducing environments such as those containing sulfuric and phosphoric acids. The molybdenum also aids resistance to pitting and crevice corrosion. The alloy’s chromium content confers resistance to a variety of oxidizing substances such as nitric acid, nitrates and oxidizing salt. The titanium addition serves, with an appropriate heat treatment, to stabilize the alloy against sensitization to inter granular corrosion.